6%-14% Nickel Content Catalyst

1.great catalytic activity 2.high mechanical strength 3.excellent thermal and coking resistance 4.NH3 Decomposing Rate:min95%

1.Product Description

6%-14% Nickel Content Catalyst is developed cooperatively by our company and chemical 

Physics Research Institute in Dalian of Chinese Academy of Sciences, for replacing G117 of Germany. 

It is provided with the properties of great catalytic activity, high mechanical strength, excellent

 thermal and coking resistance. It is used in the ammonia decomposing furnace to decompose the

NH3 and HCN etc. into N2, H2 and CO2, and so as to effectively purify the coke oven gas for the sake of environmental protection and prevent the equipment from corrosion. 

2.Technical Features

(1) Chemical reaction

 NH3 → 0.5 N2 + 1.5H22HCN + 2H2O+O2 → N2 + 5H2 + 2CO2  

(2)Technical Indexes

Type  Item	AD-946	AD-946 A	AD-946 B
Color	Grey and Black
Shape	Cylinder	Rasching Ring	Honeycomb
Size,  mm	Φ18×20	Φ18×20×5	Φ18×20
Ni Content,%	min.6	min.6	min.6
Bulk density ( g/ml)	1.4 ~ 1.6	1.3 ~ 1.5	1.2 ~1.5
Surface area,m2/g	1 ~ 3	2 ~ 4	2 ~ 5
Crushing strength (N)	1000	1000	1100
Thermal resistance, °C	min.1350	min.1350	min.1350

3.Normal Operating Conditions 

Operating Temp.	1000~1200°C
Maximum Temp.	1350°C
Pressure	0.1~1MPa
Space Velocity	1000~3000 h-1
NH3 Decomposing Rate	min.95%

  

4.Parts of Lihua Laboratory

5.Reference

General Manager Mr Aihuai Wang and vice General Manager Mr John were invited to visit US Steel Company for cooperation

and technical advice during the loading and testing of catalysts on Oct.2010

6%-14% Nickel Content Catalyst